Sign In | Join Free | My spintoband.com
China YUNCHENG CITY SHUANGMA METAL WELDING MATERIALS CO.,LTD logo
YUNCHENG CITY SHUANGMA METAL WELDING MATERIALS CO.,LTD
YUNCHENG CITY SHUANGMA METAL WELDING MATERIALS CO.,LTD Best quality and best sevice
Active Member

8 Years

Home > ER4043 >

Manufacturers of direct selling AWS ER4043 Aluminium Alloy Rod 2.4/3.2mm Made In China

Product Categories
YUNCHENG CITY SHUANGMA METAL WELDING MATERIALS CO.,LTD

Manufacturers of direct selling AWS ER4043 Aluminium Alloy Rod 2.4/3.2mm Made In China

Place of Origin : China

Brand Name : Shuangma

Certification : CE,ISO,DNV/GL

Model Number : ER4043 2.4/3.0/3.2MM

MOQ : 500kgs

Price : USD3.3/kgs FOB Shanghai

Packaging Details : 5kgs/10kgs per carton

Delivery Time : 7-15 days after confirm the order

Payment Terms : TT,LC, Western Union, D/P

Supply Ability : 300MT per month

material : aluminum alloy

color : silver

Diameter : 1.6/2.4/3.0/3.2MM

Weight : 5kg, 10kg

Contact Now

ER4043

ER4043 is a kind of aluminum & silicon alloy welding wires with 5% silicon, also name S331, and this product is of good liquidity, good forgeability, but lack of ductility. Due to the high silicon content, when used in the welding of high magnesium alloy, easily generated in the weld brittle Mg2Si, reduce the plasticity and the corrosion resistance of joint. In addition, the welding surface color dark, anodized after more different with parent metal color.

Usage: The argon arc welding of Aluminum alloy casting and workpiece is used as the filler material, special for 6061 and 6XXX series aluminum alloy, and 3XXX & 2XXX series aluminumalloy welding, widely used in ships,engine,chemistry,food,sports,uipment,mould,furniture,vessel,container,etc.

ER4043 aluminum & silicon is with high of crack resistance, but low plasticity, so for Plastic deformation joints after welding, we donor suggest it. You should strictly clean the oxide film on the edge of the workpiece and oil before welding, otherwise it will make bad weld produce and cause porosity, slag inclusion and other defects. Also you can use a plate to hold molten metal to ensure meld form.

Chemical component(wt)/%

Si

Fe

Cu

Mn

Mg

Cr

Zn

Ti

Zr

Be

Others

Others totsl

0.05

0.15

Al

4.5~6.0

0.8

0.3

0.05

0.05

0.1

0.2

0.0003

Rem.

Characteristic

Melting range

1065 - 1170°F

Electrical conductivity

42%IACS(O)

Density

2.68g/mm3

Anti corrosion performance

B(Gen) A(SCC)

The coefficient of thermal expansion (20 ℃ ~300 ℃)

22×10-6/K

Thermal conductivity (20 ℃)

170W/m·K

Wire standard

Classification:

GB10858-2008

ANSI/AWS A5.10-92

Passed ISO9001:2008 Quality Management System

The mechanical properties of the welding joints

Motherboard

Motherboard performance

Joint properties

Rm (MPa)

RP0.2 (MPa)

>A/%

Rm (MPa)

RP0.2 (MPa)

A/%

2014-T6

480

410

13

230

190

4

6061-T4

240

140

22

185

120

8

6061-T6

300

270

12

185

120

8

6063-T4

25

22

22

20

10

12

6082-T6

300

250

6

190

160

4

Specifications and packaging

Diameter /mm

Packing /Kg

MIG

0.8,0.9,1.0,1.2,1.6,2.4

0.5,2,5,6,7

TIG

1.6,2.0,2.4,3.0,3.2,4.0,5.0/1000

5,10

TIG(1000mm/5kg in plastic box/10kgCTNS)

MIG(0.5kg/2kg/7kg in plastic spool)

Manufacturers of direct selling AWS ER4043 Aluminium Alloy Rod 2.4/3.2mm Made In China


Wholesale Manufacturers of direct selling AWS ER4043 Aluminium Alloy Rod 2.4/3.2mm Made In China from china suppliers

Manufacturers of direct selling AWS ER4043 Aluminium Alloy Rod 2.4/3.2mm Made In China Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: YUNCHENG CITY SHUANGMA METAL WELDING MATERIALS CO.,LTD
*Subject:
*Message:
Characters Remaining: (0/3000)
 
Inquiry Cart 0